Adflex Q 300 F是一种热塑性聚烯烃，用于挤出或压延软膜。Adflex Q 300 F还可用作挤出应用中聚丙烯均聚物的抗冲击/增韧改性剂。例如，在捆扎应用中，它显著降低了纤维颤动，并提高了薄膜在高拉伸比下的可加工性。Adflex Q 300 F可在任何传统PP挤出生产线上以及PVC日历上加工。也可在标准LDPE或LLDPE薄膜生产线上进行吹塑。
有关法规遵从性信息，请参阅Adflex Q 300F法规事务产品管理信息/认证数据表（RAPIDS）
Adflex Q 300 F
聚烯烃
LyondellBasell Industries
产品说明：
Adflex Q 300 F is a thermoplastic polyolefin which has been developed for the extrusion or calendering of soft film. Adflex Q 300 F can also be used as impact/toughener modifier of polypropylene homopolymer in extrusion applications. In strapping applications for instance, it notably decreases fibrillation and improves the processability of the film at high drawing ratios. Adflex Q 300 F can be processed on any conventional PP extrusion line as well as on PVC calendars. It can also be blown on standard LDPE or LLDPE film lines.
For regulatory compliance information see the Adflex Q 300F Regulatory Affairs Product Stewardship Information/Certification Data Sheet (RAPIDS), which can be found on.
Adflex Q 300 F 物性表
物理性能额定值单位制测试方法
| 密度 | 0.890 | g/cm³ | ISO 1183/A |
| 熔流率（熔体流动速率） (230°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
硬度额定值单位制测试方法
| 肖氏硬度 (邵氏 D) | 36 |
| ISO 868 |
机械性能额定值单位制测试方法
| 拉伸模量 |
|
| ISO 527-2/25 |
| 0.0500 mm 1 | 200 | MPa | ISO 527-2/25 |
| 0.0500 mm 2 | 320 | MPa | ISO 527-2/25 |
| 拉伸应力 |
|
|
|
| 屈服 | 9.00 | MPa | ISO 527-2 |
| 断裂, 0.0500 mm 3 | 18.0 | MPa | ISO 527-2/500 |
| 断裂, 50.0 mm 4 | 27.0 | MPa | ISO 527-2/500 |
| 拉伸应变 |
|
|
|
| 横向流量 : 屈服, 0.0500 mm | 28 | % | ISO 527-2/500 |
| 流量 : 屈服, 0.0500 mm | 20 | % | ISO 527-2/500 |
| 断裂 | 500 | % | ISO 527-2 |
| 弯曲模量 | 330 | MPa | ISO 178 |
| Tensile Strength at Yield 5 |
|
| ISO 527-3 |
| MD | 11.0 | MPa | ISO 527-3 |
| TD | 8.00 | MPa | ISO 527-3 |
| 断裂伸长率 6 |
|
| ISO 527-3 |
| MD | 870 | % | ISO 527-3 |
| TD | 850 | % | ISO 527-3 |
薄膜额定值单位制测试方法
| 薄膜厚度 - 经测试 | 50 | µm |
|
冲击性能额定值单位制测试方法
| 悬壁梁缺口冲击强度 |
|
| ISO 180/1A |
| -50°C | 40 | kJ/m² | ISO 180/1A |
| -20°C | 70 | kJ/m² | ISO 180/1A |
| 23°C | 无断裂 |
| ISO 180/1A |
热性能额定值单位制测试方法
| 热变形温度 (0.45 MPa, 未退火) | 50.0 | °C | ISO 75-2/B |
| 维卡软化温度 | 75.0 | °C | ISO 306/A50 |
光学性能额定值单位制测试方法
| 光泽度 (45°, 50.0 µm) | 4 |
| ASTM D2457 |
| 雾度 (50.0 µm) | 95 | % | ASTM D1003 |